    FORMER  BOUNDARIES CHARACTERIZATION IN THE SUPERPLASTIC MICROSTRUCTURE OF A Zn-Al EUTECTOID ALLOY MODIFIED WITH 2%Wt OF Cu

    Thumbnail
    Ver/
    art04 - 270118-23.pdf (525.6Kb)
    art04 - 270118-23.pdf (525.6Kb)
    Fecha
    2017-10
    Autor
    Ramos, M.
    Martínez, E. E.
    Hernandez, J. L.
    Metadatos
    Mostrar el registro completo del ítem
    Resumen
    The effect of three different solutionizing and annealing heat treatments on the initial superplastic microstructure of a Zn-21Al-2Cu alloy was studied. Microstructural characterization using SEM and DRX techniques revels the presence of residual grain boundaries of a high temperature  phase (referred to as Former  Boundaries, FBs) which encompass groups of fine  (Al rich phase) and  (Zn rich phase). The origin of these arrangements may most likely be due to small deviations from the eutectoid composition as consequence of the Cu addition, which preferentially promotes the precipitation of proeutectoid phase to the high temperature phase boundaries. The final domains size only are influenced by the solutionizing treatment time, while the fine phases size only is affected by the duration of the subsequent annealing process. The presence and characteristic of his FBs could be import in order to explain possible microstructural changes, which lead to a reduction of the grain boundary sliding capacities of fine , and  phases that conduces at the early onset of a non-stable plastic flow previously observed in this alloy
    URI
    http://bdigital2.ula.ve:8080/xmlui/654321/1668
    Colecciones
    • Vol. 27, Nº 1: Enero - Abril (2018)

    DSpace software copyright © 2002-2016  DuraSpace
    Contacto | Sugerencias
    Theme by 
    Atmire
     

     

    Listar

    Todo Biblioteca DigitalComunidades & ColeccionesPor fecha de publicaciónAutoresTítulosMateriasEsta colecciónPor fecha de publicaciónAutoresTítulosMaterias

    Mi cuenta

    AccederRegistro

    Estadísticas

    Ver Estadísticas de uso

    DSpace software copyright © 2002-2016  DuraSpace
    Contacto | Sugerencias
    Theme by 
    Atmire