dc.description.abstractEl propósito de la presente investigación es caracterizar un acero inoxidable 304H expuesto a elevada temperatura (650°C) por 15 años de servicio, resaltando el estudio de la precipitación de fase sigma, convirtiendo el acero en un material frágil. Se realizó ensayo Charpy para evaluar la tenacidad al impacto, se utilizó Microscopía Óptica para identificar los precipitados y medición de dureza tanto a la fase como a la matriz, así mismo, se realizó Microscopía Electrónica de Barrido (MEB) para evaluar la superficie de fractura, realizar evaluación de la forma del precipitado y Espectrometría de dispersión de energía de rayos X (EDX) para identificar la composición química de las fases y matriz. Se determinó que las muestras con la menor tenacidad de impacto tienen partículas alargadas, agrupadas y muy finas, evidenciando que la forma y su agrupación, afecta la tenacidad, incluso los resultados de la tenacidad de impacto están por encima del umbral definido para reemplazo, pero el material presenta zonas de clivaje y agrietamiento secundario, indicando que el umbral definido no garantiza evitar una posible falla en servicio La dureza en el precipitado, es 33,2%por encima de la dureza de la matriz austenita que en adición a la alineación de las partículas y su forma, desde el punto de vista de mecánica de la fractura, permite la formación y crecimiento de grietas, afectando la tenacidad al impacto del material, lo que hace el acero inoxidable frágil. Se evidenció un agrupamiento de los precipitados, formando una especie de “rosario”, los cuales progresivamente se unen y culminan formando una grieta.en_US
dc.description.abstractThe proposal of the present investigation is to characterize a stainless steel 304H exposed to high temperature (650 ° C) for 15 years on service, highlighting Sigma phase precipitation study, changing the steel in an embritelment material.We did a Charpy test, hardness evaluation of phase and matrix, as well as scanning electron microscopy (SEM) to evaluate the fracture surface, evaluation of the shape of the precipitate and X-ray energy dispersion spectrometry (EDX) to identify the chemical composition of phases and matrix. It have been determined in samples with the lowest impact toughness have elongated, grouped and very fine particles, evidencing that shape and its grouping, affects the tenacity, even the results of the impact toughness are above defined threshold for replacement, but the material presents zones of cleavage and secondary cracking, indicating that defined threshold does not guarantee to avoid a possible failure in service. The hardness in the precipitate is 33,2% above of the austenite matrix that in addition to alignment of the particles and its shape, from the point of view of fracture mechanics, allows the formation and growth of cracks, affecting the impact toughness of the material, which it makes the stainless steel brittle. A grouping of the precipitates was evidenced, forming a kind of ‘’rosary”, which progressively join and culminate forming a cracken_US
dc.language.isoesen_US
dc.publisherUniversidad de Caraboboen_US
dc.rights.urihttp://creativecommons.org/licenses/by-nc-sa/3.0/ve/en_US
dc.subjectacero inoxidable grado 304 Hen_US
dc.subjectfase sigmaen_US
dc.subjectfragilizaciónen_US
dc.subjecttenacidad de impactoen_US
dc.subjectstainless steel 304 Hen_US
dc.subjectintermetallic phasesen_US
dc.subjectsigmaen_US
dc.subjectembrittlementen_US
dc.subjectimpact toughnessen_US
dc.titleCaracterización de un acero inoxidable 304 H expuesto a elevada temperatura por 15 años de servicioen_US
dc.title.alternativeCharacterization of an austenitic stainless steel AISI 304 H with 15 year in service exposed at high temperatureen_US
dc.typeArticleen_US


Ficheros en el ítem

Thumbnail

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem

http://creativecommons.org/licenses/by-nc-sa/3.0/ve/
Excepto si se señala otra cosa, la licencia del ítem se describe como http://creativecommons.org/licenses/by-nc-sa/3.0/ve/